Hot Air Levelling Technology Lead-Free
—  offered by  —  
Precoplat Precision Conductive Plates Technology (PCP)

The nearer the deadline draws to the compulsory
implementation of lead-free regulations (ROHS), the
greater the attempts to achieve lead-free solutions that
are comparable to the “all-purpose answer” SnPb in
terms of technology and cost. Two systems are
particularly predominant: tin/silver/copper (SnAgCu) and,
more recently, stabilised tin/copper (SnCuNi). Although
the level of efficiency of both systems is not yet completely
clear, the following presents the latest information:

 
 
 
  SnAgCu  
  There is more experience in the field of silver systems. Here, differentiation is made
between the Sn-3.5Ag-0.7Cu, Sn-4Ag-0.5Cu and Sn-3Ag-0.5Cu systems which vary in
use from continent to continent.

However, the agreed expert opinion (IPC/Soldertech-Conference Brussels 2003) is that
the technological differences between the three systems are negligible.

Sn-3.5Ag-0.7Cu is the most common alloy in Europe.

 
  SnCuNi  
  Although there are even fewer field results for the stabilised tin/copper system Sn-0.7Cu- 0.1Ni, it shows a lot of potential.

It is called “stabilised” because the addition of nickel is said to show an improved hardening reaction in soldering.

The creation of needle-structured crystals is said to alter to rounder structures, achieving an improved soldering flow for wave soldering of PCBs (reduction in torn soldering, less electrical bridging).

This alloy was developed in Japan and is supplied in Germany by the license holder, Balver Zinn.

 
  The Printed Circuit Board Manufacturer  
  The SnCuNi system is particularly interesting for the PCB manufacturer as the
investment needed to convert from conventional lead-tin techniques to tin/copper is far
lower than for facilities providing the processing technology for chemically produced
surfaces.

Because, this is also a melting pot procedure. And only the solder’s tolerance with the
dipping-container needs to be further researched.

Our company is already working on solutions with mechanical engineering
manufacturers. From May 2004, we plan to offer our customers SnCuNi is series

 
  Soldering Trials  
  As already mentioned, there has been insufficient field research. Therefore direct
comparison of soldering characteristics has been undertaken in diverse trial campaigns by expert and work groups (BDF Germany, Boeing USA).

Both systems enable smooth, shining surfaces and reliable soldering joins, using wave
soldering as well as reflow.

The tin-copper system promises advantages in terms of the copper’s peeling reactions
(leaching) on the circuit boards. The effect on the copper surface is halved.

Costs must be kept in mind. The silver system is approximately 40% more expensive than SnCuNi due to the use of precious metal; also, there is the ecological disavantage.

 
  Lead Sensitivity:  
  The problem of lead sensitivity during the lead-free conversion phase in 2006 remains
unsolved.

Structural changes in lead-free soldering caused by remains of lead (even below 0.1%
weight) in processing containers have been observed.

Structural coarseness occurs in SnAgCu if there are stressful temperature changes even well below 96 C° (degradation acceleration).

Lead secretion occurs in bordeline grains in SnCuNi systems which, under mechanical tension, can create weak spots. Splitting is possible when soldering heat cools.

 
  Conclusion:  
  There is no doubt that the “good old” lead/tin still provides the best soldering results.
However, the two procedures presented above can be improved upon.

The temperature and processing profiles in wave and reflow soldering are two points
where this could happen, so that almost the same quality could be achieved.

In spite of the limited experience in the field, in our opinion, the SnCuNi system offers
definite advantages over the silver systems both in cost and quality.


 
  The following table shows the characteristics of both systems in direct comparison:  
 
Melting point
(eutectical point)
217 C° 227 C°
Procedure characteristics Wave Badtemp.: 255 – 265 C° Badtemp.: 255 - 260 C°
Metal price 12 – 13 € 7 – 8 €
Soldering error rate compared with SnPB Equal Solder bridging, more non-soldering Equal Solder bridging, more non-soldering

 
| Precoplat Präzisions-Leiterplatten-Technik GmbH resident in 47877 Willich-Germany |
| Registered at the Krefeld District Court | Registration No. HRB 1444 | VAT-ID-No.: DE 120 156 920 |
| Management: Hildegard Völker & Andreas Brüggen | Post Address: 47805 Krefeld, Oberdiessemer Strasse 15 |
| Telephone: ++49 (0) 21 51 825 1 | Telefax: ++49 (0)21 51 932 450 | eMail: infotern@precoplat.com |

Login | Contact | Management | Imprint | Provider Identification | Terms of Trade | Technical Terms |
Data Protection  | Registration | Sitemap | Newsletter | Recommend us |
Online-Ordering | Print | FAQ |
 
Tuesday, October 24, 2017